| General |
|
|
|
|
| Density |
|
ISO 1183 |
g/cm3 |
1.04 |
| Water Absorption |
|
ASTM D 570 |
% |
0.3 |
| Rheological
|
|
|
|
|
| Melt Flow Rate (MFR) |
|
ISO 1133 |
g/10min |
23 |
| Mechanical
|
|
|
|
|
| Tensile Strength |
50 mm/min |
ASTM D 638 |
MPa |
45 |
| Strain at break |
50 mm/min |
ASTM D 638 |
% |
20 |
| Flexural Strength |
2 mm/min |
ASTM D 790 |
MPa |
69 |
| Flexural Modulus |
2 mm/min |
ASTM D 790 |
MPa |
2350 |
| Izod Impact Strength Notched |
+23°C - thickness 3.2 mm |
ISO 180/4A |
J/m |
170 |
| |
0°C - thickness 3.2 mm |
ISO 180/4A |
J/m |
100 |
| |
- 20°C - thickness 3.2 mm |
ISO 180/4A |
J/m |
70 |
| |
- 40°C - thickness 3.2 mm |
ISO 180/4A |
J/m |
50 |
| |
+23°C - thickness 4 mm |
ISO 180/1A |
kJ/m² |
13 |
| |
- 40°C - thickness 4 mm |
ISO 180/1A |
kJ/m² |
6 |
| Charpy Impact Strength, Notched |
+23°C |
DIN 53453 |
kJ/m² |
10 |
| Unnotched |
+23°C |
DIN 53453 |
kJ/m² |
NB |
| Unnotched |
- 40°C |
DIN 53453 |
kJ/m² |
NB |
| Rockwell Hardness |
scale R |
ISO 2039/2 |
kJ/m² |
R109 |
| Thermal
|
|
|
|
|
| Vicat Softening Tempreture |
10 N - 120°C/h |
ISO 306/A120 |
ºC |
99 |
| |
50 N - 120°C/h |
ISO 306/B120 |
ºC |
96 |
| Deflection temp. under load (annealed) |
1.8 MPa - 120°C/h |
ASTM D 648 |
ºC |
96 |
| Ceofficient of linear thermal expansion |
|
ASTM D 696 |
10 -5/ºC |
9 |
| Thermal Conductivity |
|
ASTM C 177 |
W/(Km) |
0.17 |
| Moulding Shrinkage |
|
ISO 294.4 |
% |
0.4-0.6 |
| Flammability
|
|
|
|
|
| Flame behavior |
thickness 1.5 mm |
UL 94 |
class |
HB |
| Glow wire test |
thickness 3 mm |
IEC 60695-2-1 |
ºC |
650 |
| Electrical
|
|
|
|
|
| Surface resistivity |
dry |
IEC 60093 |
ohm |
10+14 |
| Volume resistivity |
dry |
IEC 60093 |
ohm*cm |
10+15 |
| Dielectric strength |
dry |
IEC 60243 |
kV/mm |
30 |
| Dielectric constant (relative permittivity) |
1000 Hz - dry |
IEC 60250 |
|
3.1 |
| Dissipation factor |
1000 Hz - dry |
IEC 60250 |
|
15*10-³ |